ZrW2O8-ZrSiO4复合材料的制备及其热膨胀性能 |
Preparation and thermal properties of ZrW2O8-ZrSiO4 composite |
|
DOI: |
中文关键词: ZrW2O8 烧结 X-射线粉末衍射 热膨胀系数 |
英文关键词: ZrW2O8 sintering X-ray powder diffraction coefficient of thermal expansion |
基金项目: |
|
摘要点击次数: 2793 |
全文下载次数: 0 |
中文摘要: |
采用传统固相工艺合成ZrW2O8-ZrSiO4(体积比为1∶1)陶瓷复合材料,通过扫描电镜、和热机械分析仪分别对制备样品的断面形貌、物相组成和热膨胀性能进行表征.研究结果表明,复合材料的最佳烧结温度和时间为1 200 ℃和8 h,烧结过程中各组分之间没有发生化学反应,复合材料中仅含有原始组分ZrW2O8和ZrSiO42种物相,其在25 ~ 300 ℃的平均热膨胀系数为-0.77*10-6 K-1. |
英文摘要: |
The ZrW2O8-ZrSiO4 ceramic composites were successfully prepared by using the traditional solid-phase synthesis method in volume ratio of 1∶1.The specimens of fracture surface, phases and thermal expansion properties were characterized by way of scanning electron microscope (SEM),X-ray powder diffraction (XRD) and thermal mechanical analysis (TMA),respectively.The results show that the optimum sintering temperature and sintering time of the composite material are 1 200 ℃ and 8 h,respectively. There is none chemical reaction taking place during the sintering process,and so the composite only contains ZrSiO4and ZrW2O8 phase.The average thermal expansion coefficient is -0.77*10-6K-1from 25 ℃ to 300 ℃. |
查看全文
查看/发表评论 下载PDF阅读器 |
关闭 |